Nine Methods to improve twin screw extruder compounding performance

There are many techniques known to operators and plant engineers for increasing the performance of a twin-screw compounding extruder. Because of their informal nature,however, most of these methods do not appear in any equipment manuals. Nor are they generally mentioned in textbooks and technical papers. But sometimes attention to several small details  can add up to make a big difference in extruder performance. The tips described in this paper fall into three broad categories: processing techniques,machine modifications, and maintenance procedures.

  1. THERMAL INSULATOR GASKETS

The feed barrel section is almost always water cooled. But because this barrel is bolted flange to flange against barrel section 2, which is heated,heat is continuously transferred from the hotter to the cooler barrel  section. As a result, barrel #2 is often notable to maintain a high enough temperature. In a typical case, the operator have set point of 180 C for barrel 2 but can never get above 135 C because of heat loss to the feed barrel. The easiest solution is to install an insulator gasket between the flanges of the feed barrel and barrel 2. These gaskets are typically 1 mm thick, and we recommend stacking two together for better insulating performance. There will still be some heat conduction through the bolts and the screw shafts, but not nearly as much as without the insulation.New extruders are often supplied with the insulator in place, but many operators don’t realize its importance and throw it away when disassembling the barrels. After several years the insulator gasket should be replaced, as the material tends to degrade and crumble.

  1. SIDE STUFFING OF POWDERS(SIDE FEEDER)

Side stuffing is widely used for feeding fillers into twin-screw extruders.Many processors desire very high loadings of fillers that are often low-bulk-density (fluffy) materials. The ultimate loading attainable is usually limited by two parameters:

  1. Volumetric capacities of the side-stuffer and mainextruder screws.  The volumetric capacityis based on the free volume of the side-stuffer’s   twin screws and of the main extruder screws,as well as the rpm of both screw sets. If material is test run through the side stuffer unbolted from the extruder and discharging into a drum, it probably will easily feed a high rate of material. But when the stuffer is attached to the extruder, capacity is often limited by the amount of material the main extruder screws can accept. Consequently, it is best to for the main extruder screws to have flighted elements with a long pitch (long flight advance) at the stuffer location, extending 2D to 4D downstream of the stuffer. This is to keep the melt in the extruder moving rapidly forward to allow the maximum free volume for the filler to enter. If the screw design causes any”dam-up” of material downstream of the stuffer, it will severely limit the amount of filler that can be fed.
    B) Venting capacity to allow air to escape the extruder. The object of venting is to allow air to escape easily, while preventing large amounts of filler from being lost out the vent. The best configuration is a top vent in the barrel immediately upstream of the side stuffer. Sometimes a small half-slot vent insert can also be used in the top of the side stuffer.
    Here are some other factors to consider:
    ■feeder drop height: Ideally, the feeder should be positioned as close as possible above the side stuffer to minimize the drop height. If a fluffymaterial is allowed to drop through air, it becomes aerated to the point where its bulk density is significantly reduced. This can limit the throughput rate of the entire line.
    ■feeder agitation type: Make sure the agitator in the filler feeder isn’t aerating the material and reducing the bulk density. Many feeder manufacturer shave special agitator designs for powders.
    ■make sure stuffer hopper is vented: Along with the filler, the stuffer also introduces a lot of air into the extruder. An open top on the side-stuffer chute will take care of venting. If you have a solid cover on the chute with a round stub up and flex connector to be feeder, it’s important to also have a vent opening.
    ■around all hoppers/chutes to drain static electricity: Some materials generate static electricity from friction. Static charge can cause powder to cling to the inside surfaces of hoppers and chutes, leading to problems such as caking. An easy fix is to run a ground wire (10 gauge is recommended) from the chute to a known good ground on the machine frame.

■compressed-air blaster: If caking persists, sometimes a special solution is needed. Hopper vibrators can be used, but are tricky to size and mount. An alternative is a “blaster” with air-jet nozzles strategically placed within the wall of the chute to break up any cakes before they get too large.The air jets are connected to a solenoid valve, which is actuated by a repeat cycle timer. This lets you set both the blast period and dwell time between blasts. It’s best to have a small air accumulator tank just upstream of the solenoid valve to provide a sharp pulse of air.

  1. HIGH-PRESSURE WATER PUMP

It’s well known that turbulent flow m a pipe will induce far greater heat transfer from the pipe wall than will laminar flow. Laminar flow occurs with low fluid velocities caused by low pressure delivery. In a laminar-flow situation, a stable boundary layer develops, which acts just like an insulator between the main fluid flow and the pipe wall. “Layers” of fluid slide over adjacent layers, without mixing and without removing much heat. With turbulent flow induced by high-pressure delivery, there is a high degree of transverse momentum exchange,which breaks up the boundary layer. As a result, the violent fluid motion causes much greater heat transfer from the pipe wall to the fluid. The easiest way to induce turbulent flow in tbe barrel cooling bores is to increase tbe delivery pressure. Extruder cooling recirculation systems typically have supply pressures from 20 to 60 psi. To achieve turbulent flow, a pressure of approximately120 psi is desired. This can be attained relatively easily by changing the pumpin the recirculation system to a high-pressure type. Almost all extruder cooling system components (hoses and valves) are rated for at least 150 psi, so120 psi still allows some safety factor. The advantage will be apparent immediately in a process that is highly exothermic. Temperature zone override scan often be greatly reduced or even eliminated. A side benefit of turbulent flow is that it inhibits fouling of the cooling bores from scale buildup.

  1. ACID-FLUSH COOLING BORES

Water-cooled extruder barrels are heat exchangers, and like all other heat exchangers the coolant bores are subject to fouling from scale buildup. Most operators notice that the cooling performance of a new extruder is much better than an extruder after three or four years of running. This is because the new extruder barrel has smooth, shiny, fresh-drilled cooling bores. The older machine has a layer of crusty mineral deposits lining the bores, which act like an insulator. If left unchecked, scale buildup can lead to a much more serious problem. Eventually the cooling bores can become completely blocked so there is zero water flow. If this happens, the only solution is to remove the barrels from the extruder and drill out all the cooling bores—a time-consuming procedure.

  1. SWITCHTO SYNTHETIC GEAR OIL

The gearbox is the heart of a twin-screw extruder. If it fails, it’s likely to be expensive to repair, and it may take quite awhile. There is one thing everyone can do, easily, to avoid gearbox problems: switch to synthetic gear oil. Synthetic oil is a huge advance in lubrication technology:
■It’s more”slippery,” resulting in less friction
■Gears,bearings, and seals last longer.
■The gearbox runs cooler and quieter.
■Synthetic oil doesn’t lose viscosity from mechanical shear.
■It maintains higher viscosity at high temperatures.

■It improves the overall efficiency of the gearbox.

  • USEANTI-SEIZE LUBRICANTS

Most people in plastics are aware of the need for anti-seize lubricants.There are several different types: copper-based, molybdenum, lithium,etc. For something like a bolt thread, probably any type will work. But for extruder spline shafts the choice of anti-seize is much more critical.Screw elements fit onto the spline shafts with a very small gap tolerance, but low-viscosity polymers tend to creep down between adjacent elements and get into this gap. With time and heat, degraded polymer forms a high-strength adhesive just like an epoxy.
If screws are left together in an extruder without being taken apart periodically, they can be extremely difficult to remove from the shafts. This is why the choice of anti-seize is so important. Many types of anti-seize lubricant are acceptable for a short period of time, but over long periods at high temperature, they degrade into a fine powder. This makes them a poor choice for spline shafts, where you need the anti-seize to perform when you’re ready to disassemble the screws months or years later. After testing all theanti-seize brands on the market over a period of many years, Leistritz has found one that is ideal for this application: Fuchs Gleitmo 820, manufactured by Fuchs Lubricants in Germany.Gleitmo 820 is a white grease containing high solids. It is very slippery and is rated for up to 1150 C. What makes it perfect for spline shafts is that it doesn’t degrade into a powder. When the screw elements are removed after months of use, the Gleitmo 820 is still a slippery grease. Fuchs Lubricants has U.S.distributors and a website (fuchs.com) with technical information.

  1. PURGE OFTEN

Purging is widely used as an easy way to clean out materials from the extruder and die and to avoid a time-consuming strip down cleaning There are many types of materials used for purging, both commercial purge products and “home engineered” purges. These materials generally fall into two categories:chemical purges and mechanical abrasive purges. Many combine both chemical and abrasive actions.Chemical purges work by attacking the plastic residue like asolvent. Many of them also incorporate a foaming action and require a 5-min”soak” in tbe barrel to allow the chemical action to work.

Mechanical abrasive purges work by scouring and scrubbing material off the metal surfaces,using friction and shear. Processors do a lot of trial-and-error experimentation to find the right purge material and technique. No”magic” purge material will work best for all materials. Commercial purge products are generally more expensive than “home engineered”purges. But if you can use less material with the commercial purge, or get tbejob done quicker, the total cost may actually be less.

Processor shave run all sorts of materials through extruders, in the quest for a cheap and effective purge material. For instance,in the U.S. Midwest many operators use cattle-feed corn, because it’s readily available and does a fairly good job of scouring out the machine. Here are two effective homemade purges:
Mix #/; S0% HDPE (or another high-viscosity resin) +50% diatomaceous earth (DE): DE is finely milled fossil shells of tiny sea organisms. It is readily available in garden supply stores. DE looks like a fine powder, but the particles have very sharp, angular edges, which produce ascouring action. Processors who run sheet and film use this purge, as it can sometimes get rid of die lines, saving a lengthy die tear down.
*Mix #2; HDPE or other viscous resin with kitchen cleanser and water: Mix a slurry of water and three or four cans of Comet or Ajax kitchen cleanser in abucket. Feed HDPE at a normal purging rate and temperature, and slowly pour the slurry into the main feed port. The water in the slurry will flash to steam,which gives a very good cleaning effect combined with the abrasive in the kitchen cleanser. (Safety note: Warn any operators nearby that steam may discharge from extruder openings. Do not look into the die or vents unless wearing a full polycarbonate face sbield and long-sleeved shirt.) Probably the most important thing is to purge often. The object is to prevent old materials from being “baked on” the metal surfaces.Once this happens, purging will generally not be able to remove the material, and a manual strip down cleaning will be the only remedy. One mistake many processors make is to run the purge only at a fixed screw rpm. It’s much more effective to vary the speed, changing from low to medium to high rpm, running for perhaps30 sec at each speed. Thisinduces different shear rates against the metal surfaces, helping to dislodge old material from the walls.

  1. EFFICIENT CHANGEOVERS

Color or material changeovers tend to create problems. Extrusion people would like to always have nice long runs. But in the real world, demands from customers mean frequent changeovers to make 80 Ib of Product A, followed by 200Ib of Product B, etc. So it is important to approach changeovers in a way to minimize operator effort and problems:
■Know how critical is cleanliness to the next product to be run. There are anecdotes around any extrusion shop of somebody purging for 16 hr to avoid pulling the screws to brush them off. The point is, if you know the next product requires athorough manual brush cleaning,don’t waste time and material trying to get by with purging.
■If possible, plan runs in order of decreasing cleanliness requirements. For example, this means going from light to dark colors. That way, you should face only one difficult changeover,when going from the dark color back to a light color.
■Have written purging or strip-down procedures to run each product. This helps operators plan their time, and eliminates discussions later on about how many pounds of product have to bescrapped because the operator didn’t clean the machine properly.

  1. WARM-UP/COOL DOWN

Extrusion people tend to keep the machinery hot all the time. Operators typically turn the heat zones on the minute they come in the plant at 7:00 am.If you’re really going to start the extruder at 8:00 am, there’s nothing wrong with this. But often people get distracted with maintenance chores, and the extruder sitsidle, heated to full operating temperature for hours at a time.This is a bad practice because it allows polymer to bake onto the screws and barrels. Once baked on, the material will continue to degrade and carbonize.Purging will not remove this material. Even worse, as the extruder is running product, black specks will periodically flake off the screws and barrels,contaminating the product and causing customer complaints. The best way to handle warm-up is to plan for when you really want to start running the extruder. Then start heating up only as soon as will allow for complete warm-up plus adequate soak time. There are also preferred shutdown/cool down procedures to avoid problems with black specks. Before shutting the extruder down, it’s good practice to fill the extruder and die to the maximum degree with some inert polymer such as HDPE to “seal” the machine. The HDPE displace soxygen, and coats the metal surfaces to greatly slow down oxidation and formation of carbon. After the extruder has been “sealed,” it is better to crash cool the machine, rather than let it cool just from exposure to ambient air over the next 18 hr. Crash cooling involves turning all the temperature set points down to zero to force the cooling solenoid valves toopen. With the coolant pump running, this will force cool water through all barrel sections, bringing the temperature down quickly. Quick cool down doesn’t give the polymer a chance to degrade and carbonize