本発明は耐摩耗性高分子材料の製造方法に関し、以下の工程を含む：ステップ1：エポキシ化二ホウ化ハフニウム粉末を調製する；ステップ2：変性二ホウ化ハフニウム粉末の調製：2,2'-diaminodiphenyl disulfide in an organic solvent, stirring uniformly, adding epoxidized hafnium diboride powder, performing ultrasonic treatment, heating and stirring for reaction, collecting solid particles by suction filtration after reaction, washing with alcohol three times and drying to obtain modified hafnium diboride powder; Step 3: preparing wear-resistant polymer material: blending nylon resin and modified hafnium diboride powder in a twin-screw extruder, heating to melting, extruding and pelletizing to obtain the wear-resistant polymer material. Compared with traditional nylon materials, the polymer material prepared by the present invention not only has greatly improved mechanical strength, but also better wear resistance, high temperature resistance and low-temperature toughness.
国コード：CN
出願番号：CN202410694789.9