The present invention discloses a low-VOC, high-transparency glass fiber-reinforced PA6 material and its preparation method. The components and weight percentages of the PA6 composite material are as follows: PA6 resin 40–90 parts, glass fiber 10–60 parts, distilled water 0.1–1 part, glass fiber treatment agent 1–3 parts, lubricant 0.2–0.6 parts, antioxidant 0.2–5 parts. The glass fibers, moistened with the glass fiber treatment agent, are fed laterally. All material components undergo mixing and pelletization via a twin-vacuum parallel twin-screw extruder. The resulting material exhibits exceptional transparency, low VOC emissions, toughness, and high rigidity, making it suitable for high-end applications in extremely demanding environments.
Country Code: CN
Application Number: CN201710968121.9